最小單層冷卻時間與風扇降速保護計算器
避免微型公仔頂端或尖角在未冷卻凝固前被重複疊加而融化變形，計算切片軟體所需的最小單層冷卻時間與降速限制。
Each polymer has distinct crystallization rates and heat capacities.
Inspect layer duration in slicer preview color-coded by "Layer Time".
Your standard outer wall / perimeters printing speed.
Layer prints in 4.0s (below 8.0s target). Slicer should throttle print speed to allow cooling without heat radiation damage.
噴嘴殘熱融化風險：強烈建議啟用擦拭塔 (Prime Tower)
On extremely small features (under 3-4 seconds), slowing down the nozzle to extreme crawls keeps a 200°C+ hot aluminum block hovering directly above molten plastic, radiant-melting the layer below. The ideal remedy is to print a sacrificial prime tower or print two parts simultaneously 50mm apart to let the layer cool while the head travels.
# Slicer Cooling Configuration測量方法與操作步驟
1. 選擇線材聚合物
PLA（需強力風扇降溫）、PETG 或 ABS/ASA（微風保溫）。
2. 查看切片預覽單層時間
在切片軟體顏色預覽中找出最尖端特徵的單層耗時（秒）。
3. 套用冷卻降速參數
將計算出的最低速度限制與擦料塔建議填入切片冷卻分頁。
高分子玻璃轉移溫度冷卻公式
降速後速度 = 基本列印速度 × (當前層時間 / 目標最小時間)。
Throttled Speed = Base Speed × (Current Layer Time / Target Min Layer Time) | Critical Dwell Threshold < 3.0s使用 PLA 列印每層僅 4.0 秒的尖塔（目標最短冷卻時間 8.0 秒）於 120 mm/s：切片軟體必須將移動與擠出速度調降至 60 mm/s。低於 3.0 秒的單層需要犧牲性擦料塔以防止噴嘴輻射熱造成軟化變形。
常見問題 (FAQ)
為什麼列印細小尖端、尖頂或迷你小劍時會軟化塌陷融成一團？
切片軟體中的「最小每層時間（Minimum Layer Time）」如何防止模型過熱軟化？
犧牲引流塔（Prime Tower）如何有效解決細長件的散熱難題？
PETG 與 ABS 的最佳最小每層冷卻時間建議是多少？
模型冷卻風扇開到 100% 會導致 PLA 層間結合強度下降嗎？
相關計算工具
列印成本與售價
精確計算材料費、電費、機器折舊、雙色/多色換料沖刷耗損及蝦皮/Shopify電商平台抽成，試算實際淨利與定價。
線材重量 ↔ 長度
支援 1.75mm 與 2.85mm 規格，精準將線材克數換算為公尺長度。涵蓋 PLA, PETG, ABS, TPU 等多種聚合物比重。
剩餘線材試算
用電子秤秤出整捲重量並扣除各廠牌空盤重量（Tare Weight），精算出剩餘可用的線材克數與長度。
光固化列印成本
計算 UV 光固化樹脂模型單次列印成本、IPA 異丙醇清洗消耗、固化箱電費及整瓶樹脂可印數量。